Plastic pipe fitting

ABSTRACT

A plastic pipe element comprises an inner one-piece liner of thermoplastic material. The liner is formed so as to include at least one cylindrical leg having a free outer end and inner end disposed intermediate opposite ends of the liner. At least one pipe section is formed comprising an inner thermoplastic lining and a fiber reinforced outer layer. That pipe section is bonded to an outer surface of the cylindrical leg such that an inner end edge of the pipe section overlies the liner. A sheet of fiber reinforced thermosetting resin molding compound is applied externally around the inner end edge of the pipe section and is subjected to pressure and heat to form the sheet into a desired shape. Thereafter, the sheet is allowed to harden. Elements formed in this manner include a T-fitting, a pipe flange, a 90° fitting, a reducer fitting, a 45° fitting, and a pipe cap.

BACKGROUND AND OBJECTS OF THE INVENTION

The present invention relates to plastic piping and, in particular, toreinforced composite pipe elements.

Plastic pipe elements, such as fittings, flanges, and caps, for example,have heretofore been fabricated using various techniques intended toprovide a high-strength element presenting a continuous fluid-conductingsurface which is resistant to chemical attack by the fluid beingconducted. It has been proposed to form a fitting by molding such thatthe internal fluid-conducting portion thereof is a continuous anduninterrupted surface (no joints), but such a molding technique isrelatively expensive. Additional techniques are disclosed in thefollowing U.S. patents: U.S. Pat. No. 4,047,741 issued to Pertriaux onSept. 13, 1977; Pat. No. 3,873,391 issued to Plauka et al on Mar. 25,1975; Pat. No. 3,458,619 issued to Prochaska on Jul. 29, 1969; Pat. No.2,503,882 issued to Medford on Apr. 11, 1950; Pat. No. 2,878,038 issuedto Noland on Mar. 17, 1959; Pat. No. 3,312,765 issued to Scott on Apr.4, 1967; and Pat. No. 3,235,289 issued to Jones on Feb. 15, 1966.

The Plauka et al patent relates to the fabrication of non-linear plasticpipe fittings. The technique disclosed therein involves mitering theedges of a plurality of plastic pipe sections so that when the miterededges engage one another in complementary fashion, the pipe sectionsassume the shape of the desired fitting. The mitered edges are held inplace while a liquid coating of an elastomeric resin such as apolyurethene elastomer is applied externally to form a permanentresilient coating or band.

The Prochaska patent relates to the fabrication of plastic fittingswhich two pipe sections are mitered and fitted on mandrels to form thedesired fitting shape. The pipe sections are positioned in a hightemperature and pressure mold while thermoplastic material is injectedinto the mold to surround the fitting joint. After the assembly isremoved from the mold, the mandrels are withdrawn.

Pipes formed in the manner disclosed in Plauka et al and Prochaska wouldresult in interfaces being created at the joints where the pipes abut,which interfaces are less resistant to chemical attack. Reinforcementcan be provided by spraying or molding-on a liquid resin coating, butsuch a coating is not as strong as would be desired.

The Pertriaux patent relates to the fabrication of a plastic pipefitting by providing a mandrel having the desired fitting shape andarranging glass fibers on the mandrel. The fibers and mandrel areencased within two half shells. A thermo-setting plastics material isinjected into the half shells to coat the fibers. After the plasticsmaterial has set, the mandrel is removed.

The Noland patent relates to the fabrication of glass fiber reinforcedplastic fittings. The technique involves the formation, in halfsections, of a fitting formed of glass fiber reinforced resin material.After the half sections are fitted together, glass fiber is wound aroundthe entire fitting and is then resin impregnated.

The Scott patent involves the fabrication of plastic pipe fittings. Thetechnique involves forming straight sections of piping from aparticle-formed polymeric material. These pipe sections are mitered andthen installed on mandrels. The assembly is inserted in a hightemperature pressure mold and fused. The mandrels are eventuallywithdrawn to produce the finished product.

The Jones patent relates to the formation of butt joints on plasticpipe. In this technique the pipe sections are cut square on the ends andabutted together. Pre-preged sheets of glass cloth impregnated with athermal-setting resin are wrapped around the abutted ends. An irradiatedpolyethylene tape is spirally wound around the pre-preged sheet. Thepre-preged tape-wrapped pipes are heated to cure the resin of thepre-preged sheet and bonded to the pipe sections.

Techniques such as disclosed above which involve extensive wrappingoperations and/or the molding of a resin around formed parts, arerelatively expensive, among other shortcomings. If joints are createdwhich are exposed to the chemical being conducted, the fitting may beunduly susceptible to chemical attack.

It is, therefore, an object of the present invention to minimize orobviate problems of the type discussed above.

It is a further object of the invention to provide novel plastic pipeelements, such as fittings, flanges, and caps, and methods for producingsame.

It is an additional object of the invention to provide novel compositeplastic pipe elements which are durable, chemically resistant, andrelatively inexpensive to manufacture.

A further object of the invention is to enable such elements to beformed without a manual filament winding operation.

SUMMARY OF THE INVENTION

These objects are achieved by the present invention which involves aplastic pipe element and method of making same. In practicing theinvention, a liner of thermoplastic material is formed which includes atleast one cylindrical leg having a free outer end and an inner enddisposed intermediate opposite ends of the liner. At least one pipesection is formed comprising an inner thermoplastic lining and a fiberreinforced outer layer. That pipe section is bonded to an outer surfaceof the cylindrical leg such that an inner end edge of the pipe sectionoverlies the liner. A sheet of fiber reinforced thermosetting resinmolding compound is applied externally around the inner end edge of thepipe section and is subjected to pressure and heat to form the sheetinto a desired shape. Thereafter, the sheet is allowed to harden.

THE DRAWINGS

The objects and advantages of the invention will become apparent fromthe following detailed description of preferred embodiments thereof, inconnection with the accompanying drawings in which like numeralsdesignate like elements, and in which:

FIG. 1 is a perspective view of one form of plastic pipe elementaccording to the present invention, viz., a T-fitting which is cut awayin longitudinal section;

FIGS. 2A-2C, are longitudinal sectional views sequentially depicting thesteps in forming the T-fitting of FIG. 1, wherein FIG. 2A depicts themolded inner liner;

FIG. 2B depicts three pipe sections mounted on the liner; and FIG. 2Cdepicts a reinforcing layer covering the juncture of the pipe sections;

FIG. 3 is a front view of another form of plastic pipe element accordingto the present invention, viz., a plastic pipe flange;

FIG. 4 is a longitudinal sectional view taken along line 4--4 of FIG. 3;

FIG. 5 is a longitudinal sectional view through another form of plasticpipe element according to the present invention, viz., a 90° fitting;

FIG. 6 is a longitudinal sectional view through another form of plasticpipe element according to the present invention, viz., a reducerfitting;

FIG. 7 is a longitudinal sectional view through another form of plasticpipe element according to the present invention, viz., a 45° fitting;and

FIG. 8 is a longitudinal sectional view through another form of plasticpipe element according to the present invention, viz., a closure cap.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS OF THE INVENTION

One preferred plastic pipe element according to the present inventioncomprises a pipe fitting 10 depicted in FIGS. 1 and 2C. Such a fitting10 constitutes a T-fitting having three fluid passages 12, 14, 16 ofcircular cross-section.

Basically, the fitting comprises an internal threeway liner element 18,three intersecting pipe sections 20, 22, 24 mounted on the liner, and anouter reinforcement layer 26 surrounding the intersection of the pipesections.

The internal liner element 18 (FIG. 2A) comprises a one-piece moldedmember of suitable thermoplastic material such as PVC or CPVC, forexample, which exhibits a high degree of chemical resistance, especiallyto acids and alkalines.

The liner element is of T-shaped configuration, comprising three legs28, 30, 32, first and second ones 28, 30 of which are coaxially alignedto define a first fluid passage 34, and the third 32 forming a secondfluid passage 36 disposed at a right angle to the first passage 34. Thelegs intersect at a location intermediate the ends of the liner.

The three intersecting pipe sections 29, 22, 24 are of dual-layer,composite construction, including an inner lining 38 and an outer layer40. The inner lining is formed preferably of the same thermoplasticmaterial as the one-piece liner element 16, e.g., CPVC, PVC, etc. Inpractice, the pipe sections 20, 22, 24 are formed by molding the innerlining 38 as a thin wall thermoplastic extrusion. The extruded lining ismounted on a mandrel which is capable of being rotated at programmedspeeds for the conventional winding of the outer layer 40 whichcomprises one or more plies of glass filaments 51 shown in FIG. 9saturated with uncured thermosetting resins. These filaments arepreferably wound helically at an angle most preferably of ±54.75degrees. Upon curing and removal of the mandrel, the filament layer 40and lining 38 form a unitary composite pipe section dimensioned suchthat the inner diameter thereof is slidable over the outer diameter of arespective leg 28, 30, 32 of the liner member 16.

To assemble the lined pipe sections 20, 22, 24 onto the liner member 18,one section 24, e.g., a "stem" section, is mitered at 45° at one of itscircular ends and is inserted over the third leg 32 of the liner member.The other two pipe sections 20, 22 are abutted to form an interface 42which extends circumferentially less than 360° because each of those twopipe sections 20, 22 has an opening cut in its side wall at the pipeinner end, which opening is mitered at a 45° angle at 44. Those two pipesections 20, 22 are inserted over the first and second legs 28, 30,respectively, of the liner member 18 such that the mitered edges 44 ofthe openings abut the mitered edge of the stem section 24, whereby thecircular openings form a center axis aligned with the axis of the stemsection 32. A suitable solvent cement is applied to the outside surfacesof the legs 28, 30, 32 prior to insertion of the pipe sections 20, 22,24. Upon hardening of the cement, the inside surfaces of the pipelinings 38 are permanently bonded to the outer surface of the linermember 18.

The reinforcement layer 26 constitutes a sheet of glass reinforcedthermosetting resin molding compound. Such material can be athermosetting polyester resin such as that made for example byOwens-Corning Fiberglas Corporation under the designation SMC II.Material of this nature is typically produced by passing polyethylenefilm under a doctor blade which deposits a controlled thickness ofthermosetting resin onto the film. Continuous glass fiber strands havingbeen passed through a chopper are deposited in random orientation ontothe thermosetting resin layer. A second polyethylene film carrying asecond controlled thickness of thermosetting resin is placed atop thechopped glass. This "sandwich" of two carrier films, thermosetting resinlayers, and chopped glass 27 (FIG. 9) is passed between a series ofroller pairs which compact the sandwich, squeeze out entrapped air, andwet the glass with the resin. The compacted sandwich is then rolled-upand stored at a controlled temperature to allow the resin to chemicallythicken to a prescribed viscosity.

The sheet molding compound is cut into a pattern which enables it to bemanually applied over the T-insertion formed by the pipe sections 20,22, 24, so as to externally surround all inner end edges 42, 44 of thepipe sections, while leaving outer ends 50, 52, 54 of the pipe sectionsexposed.

The fitting is then placed in a suitable compression mold which heatsand forms the sheet molding compound to the final configuration. Thatis, the mold comprises substantially identical half sections whichtogether form a recess in the desired shape of the reinforcement layer.The sections come together in a plane containing the axes of the threepipe sections and are heatable in conventional fashion to heat the sheetmolding compound while subjecting it to sufficient pressure to form theheated and pliant compound into its final form. Preferably, the sheetmolding compound is subjected to a temperature of about 220° F.

It will be appreciated that fittings can be massproduced relativelyinexpensively in this manner while exhibiting a high degree of strengthand chemical resistance. The chemical resistance is provided by thethermoplastic pipe lining 38 and the liner member 18 which form acontinuous, uninterrupted thermoplastic internal barrier. The edgejoints 42, 44 between the various pipe sections are covered by the linermember 18 to prevent attack upon those joints by chemicals which areconducted. A high level of strength is provided by the use of filamentwound pipe 40 reinforced by the layer 26 of glass-reinforcedthermosetting resin molding compound. The latter is formed without theneed for a conventional handwinding procedure which would be relativelyexpensive. The ends of the pipe sections are conveniently left exposedfor connection to other conduit parts.

Examples of additional pipe elements which can be formed by the presentinvention are depicted in FIGS. 3 to 8.

It will be appreciated that the internal liners, pipe sections, andreinforcement layers disclosed in connection with the followingmodifications are fabricated in the manner disclosed earlier herein.

In FIG. 7, a 45° fitting 60 is depicted which includes a molded,one-piece internal liner member 62 having first and second legs 64, 66oriented at a 45° angle relative to one another.

A pair of thermoplastic lined pipe sections 68, 70 are provided whichare separately inserted over respective ones of the legs 64, 66, andbonded thereto. A mitered joint 72 between the pipe sections 68, 70 arecovered on the inside by the thermoplastic liner member 62, and on theoutside by a reinforcement layer 74 of glass reinforced thermosettingresin molding compound which externally surrounds the intersection ofthe pipe sections. The ends of the pipe sections project beyond theresin molding compound to accommodate bonding thereof to upstream anddownstream pipe elements.

In FIG. 5 there is depicted a 90° fitting 80 which directs conductedfluid to a pair of 45° turns. A one-piece interior thermoplastic liner82 includes a pair of end legs 84, 86 joined to an intermediate portion88. The legs 84, 86 each extend at a 45° angle relative to theintermediate portion 88 and at a 90° angle relative to one another.Three thermoplastic lined pipe sections 90, 92, 94 are bonded to theoutside of the liner member 82. An intermediate one 92 of the pipesections is initially installed over the intermediate portion 88 of theliner 82 and is bonded thereto. The end pipe sections 90, 94 areinstalled over the legs 86, 84 of the liner member 82 and are bondedthereto while abutting the intermediate pipe section 92 along miterededges 96, 98. A reinforcement layer 100 of glass reinforcedthermosetting resin molding compound surrounds the intersections formedby the end pipe sections 90, 94 and the intermediate pipe section 92.

In FIG. 6 a further modification is depicted of a reducer type fitting110 which conducts fluid between larger and smaller conduit diameters12, 114, respectively. A one-piece thermoplastic internal liner 116includes a pair of coaxial legs 118, 120 of different diameter. Abridging portion 122 of the liner member which joins the legs forms apair of axially spaced, annular shoulder surfaces 124, 126 each disposedin a plane perpendicular to the longitudinal axis of the fitting. A 45°mitered edge 128 interconnects those shoulders. A pair of thermoplasticlined pipe sections 130, 132 of large and small diameter are installedover the large and small diameter legs 118, 120, respectively, of theliner member. The ends of the pipe sections are not mitered, and abutagainst the shoulders 124, 126 of the bridging portion 122 of the linermember 116. The juncture where the pipe sections come together iscovered by a reinforcement layer 134 of glass reinforced polyester resinmolding compound which, when formed, presents a 45° edge in abutmentwith the 45° miter 128 of the liner member 116. The joints formed byengagement between the pipe sections 130, 132 and the liner member 116are covered on the inside by the liner member 16 on the outside by thereinforcing layer 134.

In FIGS. 3-4, a modification is disclosed wherein a pipe elementaccording to the present invention constitutes a flange 140 adapted forconnection to a corresponding flange of another pipe element (notshown). The flange 140 comprises a one-piece molded liner 142 having acylindrical leg 144 and an integrally formed lateral extension 146 ofdisc-like configuration. The leg 144 terminates at the lateral disc andthus has its inner end disposed intermediate the ends of the liner. Theextension includes an abutment face 148 extending radially outwardlyfrom an inner end of the leg. The lateral disc includes a plurality ofapertures 150 suitable for receiving mounting bolts or the like forconnection to another flange. A thermoplastic lined pipe section 152 isinstalled over the leg portion 144 of the liner member 142 and is bondedthereto. An inner end edge of the pipe section bears against theabutment face 148, thus forming a joint therewith. Surrounding thejuncture of the pipe section and liner member 142 is a reinforcementlayer 154 of glass reinforced thermosetting resin molding compound. Thereinforcement layer 154 extends along a portion of the pipe section 152,along the entire abutment face 142 of the liner member, and along acircular periphery 156 of the lateral extension. Apertures 158 areformed in the reinforcement layer 154 in alignment with the apertures150 in the liner member 142. The reinforcement layer includes gussets160 disposed circumferentially between the apertures to strengthen theflange.

In FIG. 8 there is depicted a modification of a pipe element inaccordance with the present invention which constitutes a closure cap170 capable of blocking-off one end of a pipe element. The cap comprisesan internal one-piece liner 172 of thermoplastic material. The linermember 172 is of generally cup-shaped configuration having a cylindricalleg 174 and an integral semi-spherical closure wall 176 at one endthereof. The semi-spherical wall decreases in thickness from the end ofthe leg to the peak 178 of the semisphere. At the juncture of thesemi-spherical wall with the leg, the liner member includes a circularabutment face 180 against which the inner end edge of a thermoplasticlined pipe section 182 abuts. The pipe section 182 is inserted over theleg 174 and is bonded to an outer surface thereof. Surrounding thisjoint 180 is a reinforcement layer 184 of glass reinforced thermosettingresin molding compound. The compound completely surrounds the semisphere176 and encases the joint 180 formed by the shoulder 180 and the pipesection 182.

It will be appreciated from the foregoing that in fittings, flanges,and/or caps produced in accordance with the present invention, theinterior or fluid-contacting portion of the element is defined by acontinuous uninterrupted thermoplastic barrier which resists chemicalattack. This barrier is formed by the liner member and the lining of thecomposite pipe section. The joint formed by the end of the pipesection(s) and the member against which it abuts is shielded bothinternally and externally. Internally, such joint is covered by thethermoplastic liner, and externally by the sheet molding compound. Thus,such joint is completely impervious to chemical attack. Moreover, theglass-reinforced outside layer provides substantial reinforcement forthe joint. The fitting strength is also increased by the wound filamentsof the outer ply of the pipe sections.

Although the invention has been described in connection with preferredembodiments thereof, it will be appreciated by those skilled in the artthat modifications, substitutions, additions, and deletions may be madewithout specifically departing from the spirit or scope of the inventionas defined in the appended claims.

What is claimed is:
 1. A pipe fitting comprising:a liner ofthermoplastic material which defines a fluid passage therethrough, firstand second short pipe sections, each comprising an inner thermoplasticlining and a fiber-reinforced outer layer, said outer layer beingcomprised of a plurality of reinforcement fibers embedded in andencompassed by a thermosetting resin, said fibers being individually andcontinuously wound around said pipe sections,said first pipe sectionbeing bonded to an outer surface of a first section of said liner suchthat an end edge of said first pipe section overlies said liner, saidsecond pipe section being bonded to an outer surface of a second sectionof said liner such that an end edge of said first pipe section overliessaid liner, and an external reinforcement layer of thermosetting resinhaving an external layer of reinforcement fibers embedded andencompassed therein, said external reinforcement layer externallysurrounding said end edges and being bonded to the outer surfaces ofsaid first and second pipe sections.
 2. A fitting according to claim 1,wherein said liner is formed of one-piece.
 3. A fitting according toclaim 1, wherein said end edges abut one another.
 4. A fitting accordingto claim 1, wherein said end edges abut said liner.
 5. A fittingaccording to claim 3, wherein said end edges are mitered such that saidpipe sections can be disposed at least at a 90° angle with one another.6. A fitting according to claim 1, wherein said external layerterminates short of outer ends of said pipe sections.
 7. A fittingaccording to claim 1, wherein said liner is T-shaped, including threelegs, there being three said pipe sections bonded to respective ones ofsaid legs such that end edges of said pipe sections abut one another. 8.A fitting according to claim 5, wherein said liner includes two legsmutually disposed at an obtuse angle, there being two said pipe sectionsbonded to respective ones of said legs such that end edges of said pipesections abut one another.
 9. A fitting according to claim 1, whereinsaid liner includes two legs extending from opposite ends of anintermediate section, said legs each forming an acute angle with saidintermediate section and forming a right angle with one another, therebeing three said pipe sections bonded to respective ones of said legsand intermediate section such that end edges of said pipe sections abutone another.
 10. A fitting according to claim 1, wherein said linercomprises first and second coaxial legs of different inner diameter, anda bridging section interconnecting said legs, said bridging sectionincluding a pair of shoulders, there being two said pipe sections bondedto respective ones of said legs such that end edges of said pipesections abut said shoulders.
 11. A plastic pipe fitting comprising:aone-piece liner member of thermoplastic material including at least twolegs defining a fluid-passage through the liner, at least first andsecond short pipe sections, each comprising an inner thermoplasticlining and an outer layer, said outer layer comprised of a plurality ofreinforcement fibers embedded in and encompassed by a thermosettingresin, said fibers being individually and continuously wound around saidpipe sections,said first pipe section being bonded to an outer surfaceof said first leg of said liner member such that an inner end edge ofsaid first pipe section overlies said liner member, said second pipesection being bonded to an outer surface of said second leg such that aninner end edge of said second pipe section overlies said liner member,and an external layer of thermosetting resin externally surrounding saidend edges of said pipe sections, with outer end edges of said pipesections remaining exposed, and an external layer of reinforcementfibers embedded in and encompassed by said external layer of resin, saidexternal layer being bonded to the outer surfaces of said first andsecond pipe sections.